Low Density Lathe Tool Inserts / ISO Turning Inserts High Oxidation Resistance

Basic Information
Place of Origin: China
Brand Name: Metcera
Certification: ISO
Model Number: WNMG080408-5FG
Minimum Order Quantity: 50 Pcs
Price: $0.99-$1.16/pc
Packaging Details: 10 pcs in a plastic box; 5 plastic boxes in a carton box
Delivery Time: 5-8 work days
Payment Terms: L/C, T/T, Paypal
Supply Ability: 100,000 pcs per month
Detail Information
Material: Cermet Workpiece: Forged Steel
Hardness: < 40HRC Application: Finishing
Advantage: High Oxidation Resistance / Low Density Coating Color: Gold /Grey
High Light:

lathe machine inserts

,

hard turning inserts


Product Description

 
Low Density Lathe Tool Inserts / ISO Turning Inserts High Oxidation Resistance 
 
1. Product description
Cermet is a composite material that combines ceramic and metallic materials. The metal is used as a binder for carbide. Typically, metals such as nickel and cobalt are used.
 
PVD-coated cermet has high abrasion resistance and fracture resistance thanks to the use of the PVD coating technology (Physical Vapor Deposition) on a basis material of micro-grain carbide.
 
 
2.  Advantages of Cermet

  • High quality surface on the workpiece for finishing and semi - finishing.Turning/ milling instead of grinding can be realized;
  • High oxidation resistance -- High red hardness and High cutting speed in Dry cutting (Environmentally friendly);
  • High chemical stability -- No Built - up edge (No chemical interaction between workpiece and cutting edge);
  • Low density -- Low cost , lightweight operation; Low cutting force -- Low noise machining;
  • Natural resources advantage -- less W&Co(Strategic reserve resources)needed.
  • In the long run, raw materials are easier to obtain.

 
3.  Grade Introduction of Cermet
 

 

Cermet Grade Introduction

Grade

 

Density

(g/cm3)

 

Hardness

(HRA)

Transverse

Rupture Strength

(MPa)

Fracture

Toughness

(MPa*m1/2)

Workpiece

Applications

Features

 

 

 

MC1020

 

 

 

6.8

 

 

 

92.5

 

 

 

2200

 

 

 

9.0

 

 

Carbon steel with hardness

under 28HRC, Alloyed Steel

 

 

Finishing,

Semi-finishing

Exordinary wear resistance in continous finishing machining.
Provides stable finishing to machine steel, as well as gray cast iron and sintered alloy. 
It's a high wear resistance and high cost performance uncoated materials

 

 

 

MC2010

 

 

 

6.8

 

 

 

92.8

 

 

 

2100

 

 

 

9.0

 

 

Carbon steel with hardness

under 35HRC, Alloyed Steel

 

 

Finishing,

Semi-finishing

Anti-collapse and wear resistance performance strengthened materials is utilized
which can provide extra reliable roughness for extensive cutting conditions

 

 

 

MC1120

 

 

 

6.8

 

 

 

92.5

 

 

 

2200

 

 

 

9.0

 

 

Carbon steel with hardness

under 28HRC, Alloyed Steel

 

 

Finishing,

Semi-finishing

Exordinary wear resistance in continous finishing machining with TiC/Ti(CN) coating, provides
stable finishing to machine steel, as well as gray cast iron and sintered alloy.
It's a high wear resistance and high cost performance uncoated materials

 

 

 

MC2210

 

 

 

6.8

 

 

 

92.8

 

 

 

2100

 

 

 

9.0

 

 

Carbon steel with hardness

under 36HRC, Alloyed Steel

 

 

Finishing,

Semi-finishing

High lubricant performance PVD coating is used in this grade to realize the high class machining.
It is a coated cermet with both high wear resistance to ensure high class surface machining in univeral applications

 
 
4.  Chip Breaker Introduction of Cermet
 

Low Density Lathe Tool Inserts / ISO Turning Inserts High Oxidation Resistance 0
 
 
5.  Successful Replacement Case
 
Low Density Lathe Tool Inserts / ISO Turning Inserts High Oxidation Resistance 1
 
Material of workpiece:#20 Steel
Diameter of workpiece:38mm
Insert Type:WNGM080404-5FG
Insert Grade:MC1020
Cutting Depth:1.5mm
RPM:2400r/min
Feed:400mm/min
Processing Mode:Wet
Life Time:100Pcs
Comparing to Kyocera TN60 WNMG080404-HQ:100Pcs